Low Density, Good Rebounding, Slip Resistance, Chemical Resistance, Environmental Friendly, UV Resistance, Steam Moulding&Adhesive Processing.
Sport Shoe Sole, Vibration Decoupling, Foaming Wheel, Bike Saddle, Yoga Mat, Packaging and Dunnage Trays in the Logistics, Automotive Interior Materials, etc.
| Properties | Standard | Unit | F910 | F815 | F710 | F710T | F615 | F610 |
| Density | ASTM D792 | g/cm3 | 0.11 | 0.16 | 0.14 | 0.11 | 0.15 | 0.12 |
| Hardness | - | C | 43-50 | 38-45 | 41-45 | 43-45 | 40-42 | 38-40 |
| Tensile Strength | ASTM D412 | MPa | 1.5 | 1.3 | 1.5 | 1.6 | 1.8 | 1.5 |
| Elongation at Break | ASTM D412 | % | 150 | 170 | 200 | 150 | 200 | 200 |
| Tear Strength | ASTM D624-00 | kN/m | 12 | 15 | 15 | 15 | 20 | 15 |
| Rebounding | ISO 8307 | % | 70 | 60 | 68 | 68 | 45 | 65 |
| Compression Set | 50% 16h/50℃
/After 30min Test |
% | 30 | 30 | 30 | 30 | 30 | 30 |
| Yellowing Resistance | ASTM D1148 | Grade | 4.5 | 4 | 4.5 | 4.5 | 4 | 4.5 |
NOTE: The above values are shown as typical values and should not be used as specifications.
All the products are well inspected during the production and after production. Certificate of Analysis (COA) could be provided together with the products.
100KG/bag, processed wood pallet
1. Avoid processing material above recommended thermal processing temperatures.
Good general ventilation should be sufficient for most conditions. Consider the use of local exhaust ventilation at processing emission points.
2. Avoid breathing thermal processing fumes and vapors
3. Mechanical handling equipment can cause formation of dust. Avoid breathing dust.
4. Use proper grounding techniques when handling this product to avoid electrostatic charges
5. Pellets on the floor may be slippery and cause falls
Storage recommendations: To maintain product quality, store product in a cool, dry area. Keep in a tightly sealed container.
HSE Information: Please take MSDS for reference.