Features

Excellent Aging Resistance, Oil Resistance, Hydrolysis Resistance, High Temperature Resistance, UV Resistance, Excellent Physical properties&Weathering Resistance.

Application

Hose&Tube, Film&Sheet, Fire Hose, Lay-Flat Hose for Shale Oil Frac, Oil Tank, etc.

Properties

Standard

Unit

C80

C85

C90

C95

Density

ASTM D792

g/cm3

1.15

1.15

1.15

1.15

Hardness

ASTM D2240

Shore A/D

82/-

85/-

90/-

95/-

Tensile Strength

ASTM D412

MPa

25

30

35

45

100%Modulus

ASTM D412

MPa

7

8

12

20

300%Modulus

ASTM D412

MPa

14

20

30

40

Elongation at Break

ASTM D412

550

500

400

350

Tear Strength

ASTM D624

kN/m

90

120

140

180

DIN Abrasion Loss

DIN 53516

mm3

25

25

25

25

Tg

DSC

-30

-20

-15

-8

NOTE: The above values are shown as typical values and should not be used as specifications.

Processing Guide

For optimum results, previous drying of the product during 3-4 hours at given temperature in the TDS.
The products can be used for injection molding or extrusion, and please check more details in the TDS.

 Processing Guide for Injection Molding   Processing Guide for Extrusion
Item Parameter   Item Parameter
Nozzle(℃)

Given in the TDS

  Die(℃) Given in the TDS
Metering Zone(℃)   Adapter(℃)
Compression Zone(℃)   Metering Zone (℃)
Feeding Zone(℃)   Compression Zone (℃)
Injection Pressure(bar)   Feeding Zone (℃)

Inspection

All the products are well inspected during the production and after production. Certificate of Analysis (COA) could be provided together with the products.

Packaging

25KG/bag, 1250KG/pallet or 1500KG/pallet, processed wood pallet