C Series Oil Resistance and Hydrolysis Resistance Polycarbonate-Based TPU

Product Detail

Features

Excellent Aging Resistance, Oil Resistance, Hydrolysis Resistance, High Temperature Resistance, UV Resistance, Excellent Physical properties&Weathering Resistance.

Application

Hose&Tube, Film&Sheet, Fire Hose, Lay-Flat Hose for Shale Oil Frac, Oil Tank, etc.

Properties	Standard	Unit	C80	C85	C90	C95
Density	ASTM D792	g/cm³	1.15	1.15	1.15	1.15
Hardness	ASTM D2240	Shore A/D	82/-	85/-	90/-	95/-
Tensile Strength	ASTM D412	MPa	25	30	35	45
100%Modulus	ASTM D412	MPa	7	8	12	20
300%Modulus	ASTM D412	MPa	14	20	30	40
Elongation at Break	ASTM D412	％	550	500	400	350
Tear Strength	ASTM D624	kN/m	90	120	140	180
DIN Abrasion Loss	DIN 53516	mm3	25	25	25	25
Tg	DSC	℃	-30	-20	-15	-8

NOTE: The above values are shown as typical values and should not be used as specifications.

Processing Guide

For optimum results, previous drying of the product during 3-4 hours at given temperature in the TDS. The products can be used for injection molding or extrusion, and please check more details in the TDS.

Processing Guide for Injection Molding		Processing Guide for Extrusion
Item	Parameter	Item	Parameter
Nozzle(℃)	Given in the TDS	Die(℃)	Given in the TDS
Metering Zone(℃)		Adapter(℃)
Compression Zone(℃)		Metering Zone (℃)
Feeding Zone(℃)		Compression Zone (℃)
Injection Pressure(bar)		Feeding Zone (℃)

Inspection

All the products are well inspected during the production and after production. Certificate of Analysis (COA) could be provided together with the products.